来源出版物:CORROSION SCIENCE 卷:141 页码: 168-174 DOI:10.1016/j.corsci.2018.07.014 出版年:
摘要:The effect of anodic polarization on a pre-formed oxide scale of Ni-11Fe-10Cu alloy was investigated in Na2CO3K2CO3 melt at 750 degrees C. The pre-formed oxide scale rearranged under anodic polarization and enabled the alloy as an inert anode for oxygen evolution. The anodic polarization has a positive effect on repairing defects in the original oxide scale, i.e., repair-enhancement effect, which can enhance the protectivity of an alloy substrate and eliminate further corrosion and oxidation. This study demonstrates an effective way to prepare a protective oxide scale, and reveals the rearrangement of pre-formed oxide scale under anodic polarization.
入藏号:WOS:000441682000018
文献类型:Article
语种:English
作者关键词: Anodic oxidation; Inert anode; Molten salts; Oxide scale; Rearrangement
扩展关键词: HIGH-TEMPERATURE OXIDATION; TRANSITION-METAL OXIDES; CRYOLITE-ALUMINA MELTS; INERT ANODES; NICKEL FERRITE; PART I; CORROSION; CARBONATE; BEHAVIOR; OXYGEN
通讯作者地址:Wang, DH (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Hubei, Peoples R China.
Yin, HY (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Hubei, Peoples R China.
电子邮件地址:yinhy@smm.neu.edu.cn; wangdh@whu.edu.cn
地址:
[Cheng, Xinhua; Yin, Huayi; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Hubei, Peoples R China.
[Yin, Huayi] Northeastern Univ, Sch Met, Shenyang 110819, Liaoning, Peoples R China.
影响因子:4.862
版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079
电话:027-68778381,68778284,68778296 传真:027-68778893 邮箱:sres@whu.edu.cn