博士生范金航的论文在METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE 刊出
发布时间:2018-10-12 15:16:35     发布者:易真     浏览次数:

标题:An Efficient Electrolytic Preparation of MAX-Phased Ti-Al-C

作者: Fan, JH (Fan, Jinhang); Tang, DD (Tang, Dingding); Mao, XH (Mao, Xuhui); Zhu, H (Zhu, Hua); Xiao, W (Xiao, Wei); Wang, DH (Wang, Dihua)  来源出版物:METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE  卷:49 期:5 页码: 2770-2778       DOI10.1007/s11663-018-1304-x        出版年:  OCT 2018

摘要:Large-scale deployment of MAX-phased Ti-Al-C with intriguing mechanical and physicochemical properties is significantly retarded by its harsh preparation conditions, in which costly precursors, high temperature and non-atmospheric pressure are generally imperative. We herein report an efficient electrolytic preparation of MAX-phased Ti-Al-C by direct electro-reduction of solid TiO2-Al2O3-C in molten CaCl2 at 1223 K under normal pressure. Homogeneous layered Ti3AlC2 with an oxygen content of 4300 ppm is prepared under a voltage of 3 V between the solid cathode and graphite anode for only 4 hours. The electro-reduction of TiO2-Al2O3-C exhibits a much faster speed compared with the electrolysis employing TiO2, TiO2-C and TiO2-Al2O3 as the precursors. Time-dependent electrolysis indicates that TiC (x) O (y) is the main intermediate. The generation of refractory and highly conducting TiC (x) O (y) intermediate enhances the reduction. Density functional theory simulations show a weak affinity towards oxygen of the resulting Ti3AlC2, which is beneficial to fast and thorough deoxidation. The formation of a layered structure of Ti3AlC2 is attributed to the template effect of the precursory graphite. By simply varying the precursory stoichiometry, layered Ti2AlC is also prepared. The present protocol featuring affordable feedstock, low temperature, ambient pressure, high energy efficiency and controllable stoichiometry is promising for large-scale application.

入藏号:WOS:000444765500053

文献类型:Article

语种:English

关键词:MOLTEN CALCIUM-CHLORIDE; DIRECT ELECTROCHEMICAL REDUCTION; M(N+1)AX(N) PHASES; ION BATTERIES; TI3ALC2; TITANIUM; SALTS; CARBIDE; ELECTROSYNTHESIS; COMPOSITES

通讯作者地址: Xiao, W (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Peoples R China.

电子邮件地址:gabrielxiao@whu.edu.cn; wangdh@whu.edu.cn

地址:  [Fan, Jinhang; Tang, Dingding; Mao, Xuhui; Zhu, Hua; Xiao, Wei; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Peoples R China.

影响因子:1.834


信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893    邮箱:sres@whu.edu.cn