标题: Low-temperature plasma treatment-assisted layer-by-layer self-assembly for the modification of nanofibrous mats

作者: Liu, R (Liu, Rong); Dai, JH (Dai, Jinhong); Ma, LL (Ma, Lulu); Chen, JJ (Chen, Jiajia); Shi, XW (Shi, Xiaowen); Du, YM (Du, Yumin); Li, Z (Li, Zhi); Deng, HB (Deng, Hongbing)

来源出版物: JOURNAL OF COLLOID AND INTERFACE SCIENCE  : 540  : 535-543  DOI: 10.1016/j.jcis.2019.01.054  出版年: MAR 22 2019  

摘要: To expand the template options of immersive electrostatic layer-by-layer self-assembly (LBL), which requires hydrophilic and protonation substrates, an environmentally friendly and simple plasma pretreatment that enhances the surface charge and wettability of superhydrophobic mats is employed to effectively assist LBL. With positively and negatively charged layers, chitosan (CS) and bovine serum albumin (BSA) were alternately deposited on the surface of polystyrene (PS) mats and oxygen (O-2) plasma-treated mats via electrostatic LBL. After the exposure of plasma gas at different time intervals, the zeta-potential values of the mats were distinct, and the value of the mats was -30.1 mV after treatment via O-2 plasma for 70 s, which was approximately 5 times higher than that of the pristine PS mats. In addition, the average surface roughness (Ra) of the O-2 plasma treated mats was 116.1 +/- 12.6 nm, which was higher than that of the PS mats (87.6 +/- 14.3 nm), due to the plasma etching. The water contact angle of the PS mats was 144.5 +/- 1.4 degrees, which decreased to 0 degrees within 0.33 s after O-2 plasma treatment, proving that the modified PS mats were superhydrophilic. Compared with the mats without plasma treatment, the uniform deposition of CS and BSA on O-2 plasma-treated mats was confirmed by X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy. Moreover, the mats with an enhanced surface charge and wettability after plasma treatment and LBL processing also exhibited low cell cytotoxicity and facilitated cell growth well. (C) 2019 Elsevier Inc. All rights reserved.

入藏号: WOS:000460710800055

PubMed ID: 30677606

语言: English

文献类型: Article

作者关键词: Low-temperature plasma; Enhanced surface charge; Strong wettability; Layer-by-layer; Nanofibers

地址: [Liu, Rong; Chen, Jiajia; Shi, Xiaowen; Du, Yumin; Deng, Hongbing] Wuhan Univ, Sch Resource & Environm Sci, Hubei Key Lab Biomass Resource Chem & Environm Bi, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430079, Hubei, Peoples R China.

[Dai, Jinhong; Li, Zhi] Wuhan Univ, Minist Educ, Sch & Hosp Stomatol, State Key Lab Breeding Base Basic Sci Stomatol Hu, Wuhan 430079, Hubei, Peoples R China.

[Dai, Jinhong; Li, Zhi] Wuhan Univ, Minist Educ, Sch & Hosp Stomatol, Key Lab Oral Biomed, Wuhan 430079, Hubei, Peoples R China.

[Ma, Lulu] Southern Univ Sci & Technol SUSTech, Acad Adv Interdisciplinary Studies, Shenzhen 518055, Peoples R China.

通讯作者地址: Deng, HB (通讯作者)Wuhan Univ, Sch Resource & Environm Sci, Hubei Key Lab Biomass Resource Chem & Environm Bi, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430079, Hubei, Peoples R China.

电子邮件地址: hbdeng@whu.edu.cn

影响因子:5.09


信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893    邮箱:sres@whu.edu.cn