标题:Effects of applied voltage and temperature on the electrochemical production of carbon powders from CO2 in molten salt with an inert anode作者:Tang, Diyong; Yin, Huayi; Mao, Xuhui; Xiao, Wei; Wang, D. H.
来源出版物:ELECTROCHIMICA ACTA 卷:114页:567-573 DOI:10.1016/j.electacta.2013.10.109 出版年:DEC 30 2013
摘要:With a SnO2 inert anode, amorphous carbon powders were successfully deposited on a nickel cathode by electrochemical conversion of CO2 in Li2CO3-Na2CO3-K2CO3 eutectic melt in the temperature range of 450 degrees C to 650 degrees C and under the electrolysis voltages of 3.0 V to 6.0 V. The effects of electrolysis temperature and cell voltage on the morphology and structure of the produced carbon, and on the energy consumption of the process were systematically investigated. The morphologies and particle size of the carbon products were proven to be affected by the electrolysis cell voltage and temperature. As the electrolysis condition varied, the deposited carbon exhibited different forms, including nanoparticle, nanoflake, nanosheet and heart-shape nanostructured cage, etc. The particle sizes of the obtained carbon ranged from ay. 2 mu m to 50 nm, and smaller particles were obtained at higher cell voltage and lower electrolysis temperature. The carbon product obtained at 450 degrees C under 5.5 V exhibited the highest BET surface area of 868.3 m(2) g(-1). FTIR analysis demonstrated that oxygen-containing functional groups presented on the surface of the carbon product, which was most likely due to the active dangling bond on the carbon materials. The optimized energy consumption for producing 1 kg of carbon is as low as 35.59 kWh with a current efficiency of 87.86% at 450 degrees C under a constant cell voltage of 3.5 V.
入藏号:WOS:000330487800076
文献类型:Article
语种:English
作者关键词:Carbon dioxide capture and utilization, Carbon powder, Electrochemical conversion, Molten carbonates, Inert anode
扩展关键词:ALKALI CARBONATES; IONIC LIQUIDS; CAPTURE; ELECTROLYSIS; REDUCTION; CONVERSION; MELT
通讯作者地址:Wang, D. H; Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.
电子邮件地址:wangdh@whu.edu.cn
地址:
[Tang, Diyong; Yin, Huayi; Mao, Xuhui; Xiao, Wei; Wang, D. H.]Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.
[Wang, D. H.] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China.
研究方向:Electrochemistry
ISSN:0013-4686
版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079
电话:027-68778381,68778284,68778296 传真:027-68778893 邮箱:sres@whu.edu.cn