标题: Wetting Kinetics of Molten Carbonate on Carbon.
作者: Dou, Yanpeng; Li, Peng; Du, Kaifa; Wang, Peilin; Yin, Huayi; Wang, Dihua
来源出版物: Langmuir : the ACS journal of surfaces and colloids
DOI: 10.1021/acs.langmuir.1c01886
出版年: 2021-Aug-26
摘要: he wettability of molten carbonate on carbon determines the electrochemical performances of high-temperature direct carbon fuel cells (DCFCs). However, a universal method to measure the high-temperature wettability of molten carbonate is absent and the wetting kinetics is not well understood. Herein, we develop a dispensed drop (DD) method to measure the wetting kinetics of molten carbonate (Li2CO3–Na2CO3–K2CO3, 43.5:31.5:25.0, molar ratio) on the carbon substrate at 450–750 °C under controlled atmospheres (100%Ar, 100%CO2, and 1%O2–99%N2). The measured contact angles under different conditions reveal that increasing the O2– concentration in the gas–liquid–solid (GLS) interface decreases the contact angle. In addition, elevating the temperature, introducing O2 in the gas atmosphere, or pretreating the carbon substrate can enhance the wetting kinetics of molten carbonates. The molten carbonate completely wets the carbon substrate in 150 min in Ar gas atmosphere and in 30 min in 1%O2–99%N2 gas atmosphere at 600 °C. Further, it takes only 30 min to completely wet the pretreated carbon substrate in Ar atmosphere at 600 °C. Overall, this paper offers the DD method to study the wettability of molten carbonate on the carbon substrate, which is helpful to understand the underlying wetting mechanism and engineer the electrode design for DCFCs.
地址: [Dou, Yanpeng; Li, Peng; Du, Kaifa; Wang, Peilin; Yin, Huayi; Wang, Dihua] School of Resource and Environmental Science, Wuhan University, Wuhan 430072, China
通讯作者地址: Wang, Dihua,School of Resource and Environmental Science, Wuhan University, Wuhan 430072, China
版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079
电话:027-68778381,68778284,68778296 传真:027-68778893 邮箱:sres@whu.edu.cn