标题:Electropolymerization of polypyrrole at the three-phase interline:Influence of polymerization conditions作者:Li, Min; Zhu, Hua; Mao, Xuhui; Xiao, Wei; Wang, Dihua
来源出版物:ELECTROCHIMICA ACTA 卷:92 页:108-116 出版年:MAR 1 2013
摘要:Free-standing polypyrrole film was electrosynthesized at the interface between an HClO4 aqueous solution and a pyrrole chloroform solution through a dynamic three-phase interline electropolymerization (D3PIE) process. The cyclic voltammetary measurements showed that the onset potential for the oxidation of pyrrole monomers was similar to 0.2V vs. Hg/Hg2SO4, and the radial expansion of conductive polymer film gradually increased the reaction currents. Under potentiostatic conditions, higher potentials, higher counterion (perchlorate) concentrations and higher monomer concentrations all caused a faster growth of polymer, and the aqueous perchlorate ions appeared the most sensitive factor for the reaction currents. In the initial stage of electropolymerization, the reaction currents and the diameters of polymer films increased linearly with the operating times, and a simple model can be used to describe the growth behavior of the circular polymer film. However, several factors can cause the deviation from an ideal linear relation in the later stage of electropolymerization. Higher aqueous perchlorate concentration increased the penetration amount of perchlorate ions to organic solvent phase, resulting in the longitudinal growth of PPy polymers. In addition, the prepared PPy films exhibited significantly different microstructures between the side toward water and the side toward organic solvent, and the aqueous perchlorate concentration and monomer concentration both affect the morphologies of films greatly. In order to observe a well-defined expansion of three-phase interline, lower concentrations of aqueous perchlorate ions and monomers are preferable.
入藏号:WOS:000316520100014
文献类型:Article
语种:English
作者关键词:Electropolymerization, Polypyrrole film, Three-phase junction, Supercapacitor, Three-phase electrochemistry
扩展关键词:STANDARD GIBBS ENERGIES; BAR-LIQUID INTERFACE; OXYGEN-REDUCTION; CYLINDRICAL MICROELECTRODE; CATHODE MATERIALS; ANION TRANSFER; ION TRANSFER; ELECTRODES; WATER; ELECTROCHEMISTRY
通讯作者地址:Wang, Dihua;Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.
电子邮件地址:wangdh@whu.edu.cn
地址:[Li, Min; Zhu, Hua; Mao, Xuhui; Xiao, Wei; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.
研究方向:Electrochemistry
ISSN:0013-4686
全文链接:http://www.sciencedirect.com/science/article/pii/S0013468613000352
版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079
电话:027-68778381,68778284,68778296 传真:027-68778893 邮箱:sres@whu.edu.cn