标题:Spontaneous growth of CuO nanoflakes and microflowers on copper in alkaline solutions作者: Fan, JH (Fan, Jinhang); Tang, DD (Tang, Dingding); Wang, DH (Wang, Dihua)
来源出版物:JOURNAL OF ALLOYS AND COMPOUNDS 卷:704页码:624-630 DOI:10.1016/j.jallcom.2017.02.078 出版年:MAY 15 2017
摘要: CuO with different nano-architectures was synthesized by spontaneous corrosion of copper in alkaline aqueous solutions without any additives. CuO nanoflakes were obtained by simply immersing a copper foil in NaOH solution, while flower-like architectures constructed with nanopetals were produced in Na2CO3 solution, indicating the pH value and the anions have a significant impact on the morphology and structure of CuO. The growth rate slowed down with the decrease of the alkalinity of the solution. In a more concentrated NaOH solution (1 M), polyhedron-like Cu2O was observed at the early stage before transforming into CuO nanoflakes. Based on these findings, massive production of nano-structured CuO powders was successfully realized by using copper powder as the precursor. The growing mechanism of flower-like CuO could be explained by the oriented attachment. The extensive sources of feedstock, the simple synthetic method and the uniform architecture of the products enable CuO to be utilized in a large scale.
入藏号:WOS:000396950900079
文献类型:Article
语种:English
作者关键词: CuO; Synthesis; Corrosion; Oxide; Nanomaterial; Microstructure
扩展关键词: FIELD-EMISSION; ANODE MATERIALS; CUPRIC OXIDE; NANOSTRUCTURES; FABRICATION; SUBSTRATE; NANOCRYSTALS; MORPHOLOGY; NANOSHEETS; SURFACE
通讯作者地址: Wang, DH (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.
电子邮件地址: wangdh@whu.edu.cn
地址: [Fan, Jinhang; Tang, Dingding; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.
研究方向:Chemistry; Materials Science; Metallurgy & Metallurgical Engineering
ISSN: 0925-8388
eISSN:1873-4669
影响因子:3.014
版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079
电话:027-68778381,68778284,68778296 传真:027-68778893 邮箱:sres@whu.edu.cn