博士生逄芳钊,尹华意的论文在JOURNAL OF THE ELECTROCHEMICAL SOCIETY刊出
发布时间:2022-07-15 14:35:43     发布者:易真     浏览次数:

标题: Suppressing Carbon Deposition by Introducing SiO3 (2-) in Molten CaCl2 for Efficient Electro-Deoxidation

作者: Pang, FZ (Pang, Fangzhao); Li, P (Li, Peng); Zhao, ZQ (Zhao, Zhuqing); Guo, L (Guo, Lei); Du, KF (Du, Kaifa); Deng, BW (Deng, Bowen); Wang, DH (Wang, Dihua); Yin, HY (Yin, Huayi)

来源出版物: JOURNAL OF THE ELECTROCHEMICAL SOCIETY : 169 : 6 文献号: 062504 DOI: 10.1149/1945-7111/ac7671 出版年: JUN 1 2022

摘要: Electrolysis of solid oxides in molten CaCl2 has been proven a straightforward process to extract various metals thanks to the wide electrochemical window of CaCl2 and CaO which is soluble in molten CaCl2. However, the CaO produced during the cathodic reduction of oxides not only shuttles O2-, but also captures CO2 to generate CO3 (2-) that can be reduced to carbon at the cathode, resulting in decreasing current efficiency and contaminating the cathodic products by carbon. To solve this problem, we employed CaSiO3 to replace CaO to suppress/avoid the formation of CO3 (2-) and thereafter prevent the carbon deposition. The suppression of CO3 (2-) formation is because SiO3 (2-) is thermodynamically more stable than CO3 (2-), i.e., the CO2 generated on the graphite anode can not be captured by SiO3 (2-). In molten CaCl2-8.0 wt% CaSiO3, Cr2O3 and SiO2 are reduced to Cr and Si with much less carbon deposition than in molten CaCl2. As a result, the current efficiency increases from 21.4% to 51.9% for the reduction of Cr2O3 and 37.1% to 72.2% for the reduction of SiO2. Although introducing SiO3 (2-) will slightly decrease the electrochemical window of CaCl2, it will be a promising method to avoid carbon contamination and increase current efficiency especially for Si production.

KeyWords Plus: ELECTROCHEMICAL REDUCTION; INERT ANODE; SILICON; ELECTRODEPOSITION; METAL; TITANIUM; DIOXIDE; SULFUR; METALLIZATION; VERIFICATION

地址: [Pang, Fangzhao; Li, Peng; Zhao, Zhuqing; Guo, Lei; Du, Kaifa; Deng, Bowen; Wang, Dihua; Yin, Huayi] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

[Du, Kaifa; Deng, Bowen; Wang, Dihua; Yin, Huayi] Wuhan Univ, Int Cooperat Base Sustainable Utilizat Resources, Wuhan 430072, Peoples R China.

[Wang, Dihua] Wuhan Univ, State Key Lab Water Resources & Hydropower Engn S, Wuhan 430072, Peoples R China.

通讯作者地址: Yin, HY (通讯作者)Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

Yin, HY (通讯作者)Wuhan Univ, Int Cooperat Base Sustainable Utilizat Resources, Wuhan 430072, Peoples R China.

电子邮件地址: yinhuayi@whu.edu.cn

影响因子:4.386


信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © bwin·必赢(中国)唯一官方网站
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893    邮箱:sres@whu.edu.cn